SET Proceedings 2978-4387 Caravel Press 10.65582/set.2008.185 2008.185 Oxygen permeability and phase stability of Ba0.5Sr0.5Co0.8Fe0.2O3-δ dense membrane ParkJung Hoon pjhoon@kier.re.kr KimJong Pyo BaekIL Hyun Korea Institute of Energy Research, Daejeon, Korea 24082008 7 1 978-1-995850-08-5 1348 1353 24 August 2008 © 2008 Copyright WSSET 2008

A dense membrane of perovskite Ba0.5Sr0.5Co0.8Fe0.2O3-δ has been successfully prepared by polymerized complex method. Precursor of Ba0.5Sr0.5Co0.8Fe0.2O3-δ was analyzed by thermal gravimetric analysis and XRD to investigate optimum calcination temperature. The optimum sintering temperature of precursor is between 1000 and 1100 ℃ at which single perovskite powder is obtained without impurities. The oxygen flux of of Ba0.5Sr0.5Co0.8Fe0.2O3-δ membrane increased with increasing temperature and decreasing thickness, and the oxygen permeation flux through 1.0 mm membrane with modified surface exposed to flowing air (Ph =0.21 atm) and helium (Pl =10⁻⁵ atm) was ca. 1.4 ml/cm²·min at 950 ℃. At high temperature over 850 ℃ surface reaction is more important than bulk diffusion. Membranes after permeation test were stable in view of crystal structure irrespective of surface modification but swollen part was formed in feed-side surface of non-modified membrane. Low oxygen permeation flux of non-modified membrane might be originated from low surface adsorption and barium surface diffusion in feed side.

 Ba0.5Sr0.5Co0.8Fe0.2O3-δ membrane oxygen permeation stability 24 to 27 August 2008 7th International Conference on Sustainable Energy Technologies SET2008 7 Seoul, Korea Burggraaf, A. J. and H, J., M. Bouwmeester. 1996. Fundamentals of Inorganic Membrane Science and Technology. Elsevier. ed. A. J. Burggraaf, L. Cot, Vol 4. p 435. Netherlands. Kharton, V. V., Tsipis, E. V., Yaremchenko, A. A., Marozau, I. P., Viskup, A. P., Frade, J. R. and Naumovich, E. N. 2006. Oxygen permeability, electronic conductivity and stability of La0.3Sr0.7CoO3-based perovskites. Materials Science and Engineering: B. Vol 134. No 1. pp80-88. Netherlands. Takamura, H., Enomoto, K., Aizumi, Y., Kamegawa, A. and Okada, M. 2004. Preparation and oxygen permeability of Pr-Al-based perovskite-type oxides. Solid State Ionics. Vol 175. No 1-4. pp379-382. Netherlands. Lu, H., Cong, Y. and Yang, W. S. 2006. Oxygen permeability and stability of Ba0.5Sr0.5Co0.8Fe0.2O3-δ as an oxygen-permeable membrane at high pressures. Solid State Ionics. Vol 177. No 5-6. pp595-600. Netherlands. Lu, H., Cong, Y. and Yang, W. 2007. Oxygen permeability and improved stability of a permeable Zr-substituted perovskite membrane for air separation. Materials Science and Engineering: B. Vol 141. No 1-2. pp55-60. Netherlands. Park, J. H. and Park, S. D. 2007. Oxygen permeability and structural stability of La0.6Sr0.4Co0.2Fe0.8O3-d membrane. Korean J. Chem. Eng. Vol 24. No 5. pp897-905. Korea. Wang, H., Cong, Y. and Yang, W. 2003. Investigation on the partial oxidation of methane to syngas in a tubular Ba0.5Sr0.5Co0.8Fe0.2O3-δ membrane reactor. Catalysis Today. Vol 82. No 1-4. pp157-166. Netherlands.